Substrate Material List

Material

Structure

Orientation

Melting Point

Density 

Hardness

Index of Refraction

Thermal Expansion Coefficient (/K)

Dielectric Constants

Maximum Size

Typical Size

LaAlO3

≈Cubic

a=3.821Å

<100>

<110>

<111>

2100℃

6.52 g/cm3

6.5 Mohs

1.80

9.2 x 10^-6

24.5

Φ3″

Φ3″ x 0.5 mm

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

LSAT

(LaAlO3)0.3
(Sr2AlTaO8)0.7

Cubic

a=3.868Å

<100>

<110>

<111>

1840℃

6.74 g/cm3

6.5 Mohs

10 x 10^-6

22

Φ2″

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

SrTiO3

Cubic

a=3.90Å

<100>

<110>

<111>

2050℃

5.175 g/cm3

6 Mohs

2.409

10.4 x 10^-6

300

Φ30 mm

10 x 10 x 0.5 mm

10 x 5 x 0.5 mm

MgO

Cubic

a=4.216Å

<100>

<110>

<111>

2852℃

3.58 g/cm3

5.5~6 Mohs

1.58

12.8 x 10^-6

9.80

50 x 50 mm

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

YSZ

Cubic

c=5.125Å

<100>

<110>

<111>

2500℃

5.80 g/cm3

7 Mohs

1.96

10.3 x 10^-6

27

Φ2″

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

KTaO3

Cubic

a=3.984Å

<100>

<110>

<111>

1352℃

7.03 g/cm3

6 Mohs

2.00

4.03 x 10^-6

20 x 20 mm

20 x 20 x 0.5 mm

10 x 10 x 0.5 mm

10 x 5 x 0.5 mm 

SrLaAlO4

M4

a=3.756Å

c=12.63Å

<001>

1650℃

5.92 g/cm3

6 Mohs

<100> 10.05 x 10^-6

<001> 18.9 x 10^-6

16.8

Φ20 mm

10 x 10 x 0.5 mm

10 x 5 x 0.5 mm

YAlO3

Orthorhombic

a=5.1796Å

b=5.3286Å

c=7.3706Å

<100>

<010>

<001>

1870℃

5.37 g/cm3

8.5 Mohs

4.2 x 10^-6//a  

11.7 x 10^-6//b

5.1 x 10^-6//c

Φ30 mm

10 x 10 x 0.5 mm

Φ30 x 0.5 mm

MgAl2O4

Cubic

a=8.083Å

<100>

<110>

<111>

2130℃

3.60 g/cm3

7.5~8 Mohs

1.71

9.65

Φ2″

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

Material

Structure

Orientation

Melting Point

Density 

Hardness

Index of Refraction

Thermal Expansion Coefficient (/K)

Dielectric Constants

Maximum Size

Typical Size

LaAlO3

≈Cubic

a=3.821Å

<100>

<110>

<111>

2100℃

6.52 g/cm3

6.5 Mohs

1.80

9.2 x 10^-6

24.5

Φ3″

Φ3″ x 0.5 mm

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

LSAT

(LaAlO3)0.3
(Sr2AlTaO8)0.7

Cubic

a=3.868Å

<100>

<110>

<111>

1840℃

6.74 g/cm3

6.5 Mohs

10 x 10^-6

22

Φ2″

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

SrTiO3

Cubic

a=3.90Å

<100>

<110>

<111>

2050℃

5.175 g/cm3

6 Mohs

2.409

10.4 x 10^-6

300

Φ30 mm

10 x 10 x 0.5 mm

10 x 5 x 0.5 mm

Nb:SrTiO3

Fe:SrTiO3

Nd:SrTiO3

Cubic

a=3.90Å

<100>

<110>

<111>

2050℃

5.175 g/cm3

6 Mohs

2.409

10.4 x 10^-6

300

Φ30 mm

10 x 10 x 0.5 mm

10 x 5 x 0.5 mm

Al2O3

M6

a=4.758Å

c=12.99Å

<0001>

<11-20>

<10-10>

<1-102>

2040℃

3.97 g/cm3

9 Mohs

1.77

7.50 x 10^-6

9.4@A-axis

11.58@C-axis

Φ180 mm

Φ50.8 x 0.5 mm

Φ100 x 0.5 mm 

10 x 10 x 0.5 mm

MgAl2O4

Cubic

a=8.083Å

<100>

<110>

<111>

2130℃

3.60 g/cm3

7.5~8 Mohs

1.71

7.45 x 10^-6

Φ2″

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

GGG

Cubic

a=12.37Å

<100>

<110>

<111>

1860℃

7.05 g/cm3

6~7 Mohs

1.95

Φ2″

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

TiO2

M4

a=4.593Å

c=2.958Å

<100>

<001>

<110>

<111>

1840℃

4.26 g/cm3

7 Mohs

2.72

Φ23~25 mm 

10 x 10 x 0.5 mm

10 x 5 x 0.5 mm

TGG

Cubic

a=12.355

Å

<100>

<110>

<111>

1725℃

7.13 g/cm3

8 Mohs

1.954

Φ30 mm

Φ30 x 0.5 mm

10 x 10 x 0.5 mm

5 x 5 x 10 mm

Material

Structure

Orientation

Melting Point

Density 

Hardness

Thermal Expansion Coefficient (/K)

Lattice Mismatch for GaN

Maximum Size

Typical Size

Al2O3

M6

a=4.758Å

c=12.99Å

<0001>

<11-20>

<10-10>

<1-102>

2040℃

3.97 g/cm3

9 Mohs

7.50 x 10^-6

16.1%@<0001>

Φ180 mm

Φ50.8 x 0.5 mm

Φ100 x 0.5 mm 

10 x 10 x 0.5 mm

Si

Cubic

a=5.0430Å

<100>

<110>

<111>

1415℃

2.33 g/cm3

5.5~6 Mohs

2.59 x 10^-6

20.5%@<111>

50 x 50 mm

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

GaAs

Cubic

a=5.653Å

<100>

1238℃

5.31 g/cm3

6.5 Mohs

5.75 x 10^-6

19.9%@<111>

Φ4″

Φ4″ x 0.625mm

Φ2″ x 0.35mm

LiAlO2

M4

a=5.17Å

c=6.26Å

<100>

<001>

<110>

<111>

1900℃

2.62 g/cm3

7.5 Mohs

7.1 x 10^-6

1.4%@<100>

Φ2″

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

MgAl2O4

Cubic

a=8.083Å

<100>

<110>

<111>

2130℃

3.60 g/cm3

7.5~8 Mohs

7.45 x 10^-6

9%@<111>

Φ2″

Φ2″ x 0.5 mm

10 x 10 x 0.5 mm

SiC

M6

a=3.080Å

c=15.12Å

<0001>

<11-20>

<10-10>

2830℃

3.217 g/cm3

9.2 Mohs

4.2 x 10^-6@c

3.5%@<0001> 

Φ4″

Φ2″ x 0.33 mm

10 x 10 x 0.33 mm

ZnO

M6

a=3.325Å

c=5.213Å

<0001>

<11-20>

<10-10>

1975℃

5.605 g/cm3

4.5 Mohs

2.92 x 10^-6@c

2.0%@<0001>  

Φ25 mm 

10 x 10 x 0.5 mm

20 x 20 x 0.5 mm

GaN

M6

a=0.3189Å

c=0.5186Å

<0001>

1700℃

6.1 g/cm3

8 Mohs

3.17 x 10^-6@c

5.59 x 10^-6@a

0%@<0001>

Φ2″

Φ2″ x 0.3 mm

10 x 10 x 0.3 mm

Material

Structure

Orientation

Melting Point

Density 

Band Gap

Conductivity Type

Dopant

Resistivity

Maximum Size

Typical Size

Si

Cubic

a=5.0430Å

<100>

<110>

<111>

1415℃

2.33 g/cm3

1.124 ev

N or P

undoped

>1000 Ώ.cm

Φ6″

Φ2″ x 0.5 mm

Φ3″ x 0.5 mm

Φ4″ x 0.5 mm

N

P

0.001~40 Ώ.cm

P

B

100~10000 Ώ.cm

Ge

Cubic

a=5.6575Å

<100>

<110>

<111>

937.4℃

5.323 g/cm3

0.66 ev

/

undoped

>30 Ώ.cm

Φ4″

Φ2″ x 0.5 mm

Φ3″ x 0.5 mm

Φ4″ x 0.5 mm

N

Sb

0.01~30 Ώ.cm

P

In or Ga

0.01~30 Ώ.cm

GaAs

Cubic

a=5.653Å

<100>

1238℃

5.31 g/cm3

1.424 ev

N

undoped

>10^7 Ώ.cm

Φ4″

Φ2″ x 0.35 mm

Φ4″ x 0.625 mm

Si

<0.1 Ώ.cm

InP

Cubic

a=5.869Å  

<100>

1600℃

4.79 g/cm3

1.344 ev

N

undoped

Φ3″

Φ2″ x 0.5 mm

Φ3″ x 0.5 mm

S or Fe

P

Zn

InAs

Cubic

a=6.058Å

<100>

942℃

5.66 g/cm3

0.45 ev

N

undoped

Φ3″

Φ2″ x 0.5 mm

Φ3″ x 0.5 mm

S or Sn

P

Zn

GaSb

Cubic

a=6.094Å

<100> 

712℃

5.53 g/cm3

0.67 ev

P

undoped

Φ3″

Φ2″ x 0.5 mm

Φ3″ x 0.5 mm

Zn

N

Te

Material

Structure

Orientation

Melting Point

Density 

Transmission Range

Typical Size

NaCl

Cubic

a=5.642Å

<100>

<110>

<111>

804℃

2.16 g/cm3

0.26~22 um

10 x 10 x 2.0 mm

20 x 20 x 2.0 mm

KCl

Cubic

a=6.291Å

<100>

<110>

<111>

770℃

1.98 g/cm3

0.20~27.5 um

10 x 10 x 2.0 mm

20 x 20 x 2.0 mm

KBr

Cubic

a=5.596Å

<100>

<110>

<111>

734℃

2.75 g/cm3

0.20~34 um

10 x 10 x 2.0 mm

20 x 20 x 2.0 mm