OST Photonics offer SiC wafers for semiconductor industry. There are two conduct types of SiC materials for you to choose from: N-type 4H-SiC (Conductivity Type) and high purity semi-insulating (HPSI) 4H-SiC. High purity semi-insulating SiC wafers is mainly used in 5G communication applications. It has the advantages of improving the radio frequency range, ultra-long distance recognition, anti-interference, high-spee...
OST Photonics offer SiC wafers for semiconductor industry. There are two conduct types of SiC materials for you to choose from: N-type 4H-SiC (Conductivity Type) and high purity semi-insulating (HPSI) 4H-SiC. High purity semi-insulating SiC wafers is mainly used in 5G communication applications. It has the advantages of improving the radio frequency range, ultra-long distance recognition, anti-interference, high-speed and large-capacity information transmission, and is regarded as the most ideal material for making microwave power devices. N-type SiC wafer is mainly used in new energy vehicles, high voltage transmission and transformation stations, white goods, high-speed trains, motors, photovoltaic inverter, pulse power supply and other fields, it has the advantages of reducing equipment energy loss, improving equipment reliability, reducing equipment volume, improving equipment performance and so on, it has irreplaceable advantages in the production of power electronic devices.
N-type 4H-SiC Wafers (Conductivity Type) | |||||
Diameter | 2”-50 .8 mm | 4″- 100.0 mm | 6″- 150.0 mm | 8”-200.0 mm | |
Thickness | 350μm（DSP） | 500μm（DSP） | |||
Surface Orientation | Off-Axis:<0001> 4 ° toward <11- 20> ± 0 . 5° | ||||
Primary Flat Orientation | Parallel to <1 1 -20 > ±1 ° | < 1-100> ± 1 ° | |||
Primary Flat Length | 16.0 mm | 32 . 5 mm | 47.5mm | Notch | |
Secondary Flat Orientation | Silicon face up: 90.0 ˚ CW from Primary ± 5.0˚ | N/A | N/A | ||
Secondary Flat Length | N/A | 18.0 mm | N/A | N/A | |
Resistivity | 0 . 014 ~ 0 . 028 Ω . cm | ||||
Front Surface | Si-Face : CMP , Ra<0 . 2nm | ||||
Back Surface | C-Face : optical polish, Ra<0 . 5nm | ||||
Laser Marking | Back side : C-Face | ||||
TTV | ≤ 10 μm | ≤ 15 μm | ≤ 15 μm | ≤ 20 μm | |
BOW | ≤ 25 μm | ≤ 30μm | ≤40 μm | ≤ 60μm | |
WARP | ≤ 30μm | ≤ 40 μm | ≤ 60μm | ≤ 80μm | |
Edge Excluding | ≤ 3 mm | ||||
High Purity Semi-insulating (HPSI) 4H-SiC Wafers | |||||
Diameter | 2”- 50 .8mm | 3”- 76.2 mm | 4”- 100mm | 6”-150mm | 8”-200mm |
Thickness | 500μ m (DSP) | ||||
Surface Orientation | <0001> ± 0 . 25 ° | ||||
Primary Flat Orientation | < 1- 100 > ±1° | ||||
Primary Flat Length | 16.0 mm | 22.0mm | 32 .5mm | Notch | Notch |
Secondary Flat Orientation | Silicon face up: 90.0 ˚ CW from Primary ± 5.0˚ | N/A | N/A | ||
Secondary Flat Length | 8mm | 11mm | 18 mm | N/A | N/A |
Resistivity | > 1 E7 Ω .cm | ||||
Front Surface | Si- Face: CMP, Ra<0 . 2nm | ||||
Back Surface | C-Face：CMP,Ra<0.2nm | C-Face polished. Ra＜5nm | |||
Laser Marking | Back side: C-Face | ||||
TTV | ≤10 μm | ≤15 μm | ≤15 μm | ≤15 μm | ≤20 μm |
BOW | ≤25 μm | ≤25 μm | ≤30μm | ≤45 μm | ≤ 65μm |
WARP | ≤ 30μm | ≤35μm | ≤40 μm | ≤60μm | ≤70 μm |
Edge Excluding | ≤ 3 mm | ||||
Special Polytype SiC Wafers (6H-N/4H-P/6H-P/3C-N) | |||
Dimensions | 10 * 10 mm | 2”- 50 .8mm | 4”- 100mm |
Thickness | 350μm(DSP) | ||
Polytype | 6H/4H-P/6 H-P/3C-N | ||
Surface Orientation (6H-N/4H-P/6H-P) | Off Axis: 0 . 0 °- 8 . 0 °toward < 11 – 20 > ± 0 . 5° | ||
Surface Orientation (3C-N) | On axis : <0001 > ± 0 . 5 ° | ||
Resistivity (6H-N/4H-P/6H-P) | ≤ 0 . 5 Ω · cm | ||
Resistivity (3C-N) | ≤ 1 . 0 mΩ · cm | ||
Front Surface | Si- Face: CMP, Ra<0 . 5nm | ||
Back Surface | C-Face: ptical polish, Ra< 1 .0 nm | ||
Laser Marking | Back side : C- Face | ||
TTV | ≤ 5 μ m | ≤ 10 μ m | ≤ 15 μ m |
BOW | ≤ 15 μ m | ≤ 25 μ m | ≤ 25 μm |
WARP | ≤ 30μ m | ≤ 30μ m | ≤ 40 μ m |
HPSI 4H-SiC Ultra-thin Wafer | ||||
Diameter | 2”- 50 .8mm | 4”- 100mm | 6”- 150mm | |
Dimensions | 50.8*50.8mm/76.2*76.2mm/100*100mm | |||
Thickness | 150μ m /200μ m /250μ m /350μ m | |||
Surface Orientation | {0001} ± 0 . 25 ° | |||
Primary Flat Orientation | < 1- 100> ±1° | |||
Primary Flat Length | 16.0 mm | 32 .5mm | Notch | |
Secondary Flat Orientation | Silicon face up: 90.0 ˚ CW from Primary ± 5.0˚ | N/A | ||
Secondary Flat Length | 8mm | 18 mm | N/A | |
Resistivity | > 1 E7 Ω .cm | |||
Surface finish | Polished, Ra≤ 10nm | Ultrathin， Ra<20nm | ||
Laser Marking | Back side: C-Face | |||
TTV | ≤15 μm | ≤20 μm | ≤30μm | |
Edge Excluding | ≤ 3 mm | |||
Silicon Carbide Single Crystal | |
Crystal Structure | Hexagonal Crystal |
Band gap (eV) | 3 .26 eV |
Melting Point (℃) | 2730 ℃ |
Mohs Hardness (mohs) | 9.2 |
Heat Conductivity (W·cm^-1· ℃^-1) | 4. 9 W·cm^-1· ℃^-1 |
Coefficient of Thermal Expansion (℃^-1) | 4.7 x 10^-6 |
Lattice Constant (nm) | a ＝0 .3076 c ＝ 0 .5048 |
Electronic Mobility (cm^-2.V^-1.s^-1) | 720^a 650^c |
Disruptive Field (MV· cm^-1) | 3.1 |
JFM Index (power) | 410 |
BFM Index (SW) | 290 |
BHFM Index (RF) | 34 |
Refractive Index | 2.6767 ~ 2.6480 |